Precyclic-loading-induced stress corrosion cracking of pipeline steels in a near-neutral-pH soil environment

From National Research Council Canada

DOIResolve DOI: https://doi.org/10.5006/1.3277644
AuthorSearch for: ; Search for: ; Search for: ; Search for: ; Search for:
FormatText, Article
Subjectcrack initiation; cyclic loading; near-neutral-pH stress corrosion cracking; pipeline steel; stress corrosion cracking
Abstract
Two pipeline steels of different grades were used to study the effect of cyclic loading prior to corrosion exposure upon the initiation of stress corrosion cracks in a near-neutral-pH soil environment. A cyclic loading scheme was constructed based on pressure fluctuation data collected on operating pipeline systems. The specimen surface was either mirrorpolished or polished to a 600-grit finish. It was found that precyclic loading caused the formation of microcracks on the specimen surface during subsequent corrosion exposure under constant load and under mild cathodic polarization. No such microcracks occurred at the open-circuit potential because of uniform corrosion. For specimens polished to a 600-grit finish, the microcracks were either inclined at 45° to the loading direction or aligned along the polishing scratches; for mirror-polished specimens, only microcracks inclined at 45° were observed. The formation of microcracks is attributed to the presence of localized deformation, such as persistent slip bands. These microcracks established the site for crack initiation and facilitated the development of stress corrosion cracking during subsequent slow strain rate testing.
Publication date
PublisherNational Association of Corrosion Engineers
In
  • Corrosion 58, no. 6: 526–534.
LanguageEnglish
Peer reviewedYes
NRC publication
This is a non-NRC publication

"Non-NRC publications" are publications authored by NRC employees prior to their employment by NRC.

NPARC number23001906
Export citationExport as RIS
Report a correctionReport a correction (opens in a new tab)
Record identifier24dad30a-2b4a-42b0-a8d1-a9f157128862
Record created2017-05-23
Record modified2020-03-30
Report a problem on this page
Date modified: