A study of stress-corrosion crack propagation in 2024-T351 aluminium alloy by acoustic emission

From National Research Council Canada

DOI	Resolve DOI: https://doi.org/10.1179/cmq.1984.23.1.51
Author	Search for: Blain, J.¹; Search for: Masounave, J.¹; Search for: Dickson, J. I.
Affiliation	National Research Council of Canada
Format	Text, Article
Abstract	The acoustic emission associated with stress-corrosion cracking (SCC) of 2024-T351 aluminium alloy for SL and ST orientations in 3% NaCl solution was studied, in parallel with measurements of SCC velocities. The log velocity vs stress intensity, K, curves showed stage I and stage II (plateau) behaviour. The acoustic emission rate normalized per unit of crack advance was similar for both SL and ST orientations and was constant until K values ≃1.8 times the value at which stage II started. The subsequent increase in normalized emission rate coincided with a significant increase in the amount of crack surface produced per unit of crack advance. The present results indicate that the same cracking mechanisms operate during stages I and II. The signatures of the acoustic signals recorded employing a resonant transducer during corrosion and during SCC appeared identical, suggesting that similar acoustic emission sources may be responsible.
Publication date	1984-01
Publisher	Taylor and Francis
In	Canadian Metallurgical Quarterly 23, no. 1: 51–57.
Language	English
Peer reviewed	Yes
NRC number	CNRC 26658 NRC-IGM83-205-436
NPARC number	23004061
Export citation	Export as RIS
Report a correction	Report a correction (opens in a new tab)
Record identifier	31adc3d6-78c5-45b2-8e01-657ae8f5bc92
Record created	2018-09-21
Record modified	2020-03-13

Date modified:: 2024-07-17