Investigation of the feedstock deposition behavior in a cold sprayed 316L/Fe composite coating

From National Research Council Canada

Download	View author's version: Investigation of the feedstock deposition behavior in a cold sprayed 316L/Fe composite coating (PDF, 1 MB)
DOI	Resolve DOI: https://doi.org/10.1016/j.surfcoat.2017.12.063
Author	Search for: Chu, Xin; Search for: Chakrabarty, Rohan; Search for: Che, Hanqing; Search for: Shang, Lihong; Search for: Vo, Phuong¹; Search for: Song, Jun; Search for: Yue, Stephen
Name affiliation	National Research Council of Canada. Automotive and Surface Transportation
Format	Text, Article
Journal title	Surface & Coatings Technology
ISSN	0257-8972 1879-3347
Volume	337
Pages	53–62
Subject	cold spray; mixed powder; deposition behavior; splat test; deformation; adhesion
Abstract	Mixing powders in cold spray is a straightforward method to produce composite coatings, but a direct interpretation of the mixed powder deposition behavior from coating microstructure is often difficult. In this study, to investigate the feedstock deposition behavior in a cold sprayed 316L-10 wt% Fe (10Fe) metal-metal composite coating, splats deposited onto the as-polished 316L and Fe coatings with four types of impact scenarios were studied: (i) 316L on 316L, (ii) 316L on Fe, (iii) Fe on 316L, and (iv) Fe on Fe. The splat flattening ratio and coating crater depth/diameter were measured using a light optical microscope (LOM) and an optical profilometer to evaluate the degrees of particle and coating deformation. Finite element (FE) simulations were performed to obtain the splat rebound behavior during impact. A modified ball bond shear test was performed to determine the adhesion strength/energy of the cold spray splats. Results reveal distinct interparticle bonding features in the 10Fe coating, especially at the mixed 316L/Fe interfaces where a preferential location of inter-lamellar cracks can be seen. Similar bonding features were also observed in the deposited splats, indicating the splat on coating tests to be indicative of the coating build-up process. Finally, the feedstock deposition behavior in the 10Fe coating was explained through splat characterizations and FE simulations from hardness, surface oxide layer and particle morphology.
Publication date	2017-12-29
Publisher	Elsevier
Language	English
Peer reviewed	Yes
NRC number	NRC-AST-054
NPARC number	23003119
Export citation	Export as RIS
Report a correction	Report a correction
Record identifier	3ca741d4-b36a-4973-a6dc-9de1e6f8077d
Record created	2018-04-24
Record modified	2020-03-16

Report a problem on this page

Date modified:: 2021-04-17