Fatigue life prediction of welded joints using the effective stress intensity factor range

From National Research Council Canada

AuthorSearch for: 1; Search for: 1; Search for:
Affiliation
  1. National Research Council of Canada
FormatText, Article
ConferenceThe Mechanism of Fracture : Proceedings of the fracture-mechanism program and related papers presented at the International Conference and Exposition on Fatigue, Corrosion Cracking, Fracture Mechanics, and Failure Analysis, 2-6 December 1985, Salt Lake City, Utah, USA
Abstract
Since the early 70's, LEFM concepts have been applied to welded joints and have provided a more reliable fatigue life prediction method. However, even today, very little information is available on the effects of nothch plasticity and welding residual stress for the practical problem of a crack propogating from the weld toe
Publication date
PublisherAmerican Society for Metals
In
  • International Conference and Exposition on Fatigue, Corrosion Cracking, Fracture Mechanics, and Failure Analysis: 245–253.
LanguageEnglish
Peer reviewedYes
NRC numberCNRC 25087
NRC-IGM86-203-254
NPARC number23004866
Export citationExport as RIS
Report a correctionReport a correction (opens in a new tab)
Record identifier55986807-8a53-4d86-8df4-d0a85d9f4314
Record created2019-01-07
Record modified2020-03-17
Date modified: