| Abstract | Young's modulus and internal friction were measured in polycrystalline NB₃Sn between 6 and 300K. Below the martensitic transformation temperature a large rise in internal friction is observed, in agreement with recent observations. In this temperature range, the internal friction is found to be nearly independent of frequency, a behavior consistent with stress-induced wall motion between domains of the tetragonal phase as the main source of relaxation. Internal friction peaks observed at 140 and 260K in Nb/Nb₃Sn composite tapes are tentatively attributed respectively to an α peak in Nb and hydrogen in the Nb₃Sn layer. Annealing at 750 °C for 1/2h is found to decrease the transformation temperature from 49 to 40K, and to modify the softening of Young's modulus in this temperature range. Young's modulus at 6K is 46% of room temperature value and is unchanged by the annealing treatment. |
|---|
| Publication date | 1981-10-01 |
|---|
| Publisher | EDP Sciences |
|---|
| In | |
|---|
| Language | English |
|---|
| Peer reviewed | Yes |
|---|
| NRC number | CNRC 18965
NRC-IGM81-401-355 |
|---|
| NPARC number | 23004016 |
|---|
| Export citation | Export as RIS |
|---|
| Report a correction | Report a correction (opens in a new tab) |
|---|
| Record identifier | 70037017-c937-479c-a30e-c05d419c086a |
|---|
| Record created | 2018-09-17 |
|---|
| Record modified | 2020-03-13 |
|---|