Characteristics of electron beam welded CA6NM

From National Research Council Canada

AuthorSearch for: ; Search for: 1 ; Search for: ; Search for: ; Search for:
Name affiliation
  1. National Research Council Canada. Aerospace
FormatText
TypeArticle
Proceedings titleProceedings of Materials Science and Technology
ConferenceMaterials Science and Technology 2013: Advances in Hydroelectric Turbine Manufacturing and Repair, October 27-31, 2013, Montreal Canada
Pages720–732; # of pages: 13
Abstract
In this study, the viability of thick-gauge section assembly for hydroelectric turbine manufacture was considered by electron beam welding CA6NM martensitic stainless steel, a widely utilized hydro-turbine cast material. Particularly, bead-on-plate trials on 60 mm-thick CA6NM plates were carried out using a 42 kW high vacuum electron beam welding system. The influence of the heat input, beam position, beam oscillation (XSF-YSF), and in-situ pre-heating conditions on the characteristics of the weldments, such as the bead geometry, weld integrity, fusion zone and HAZ microstructures and hardness were evaluated. A relationship between the welding parameters and the resulting depth of penetration was established. A methodology for in-situ heating of the thick-gauge section prior to welding was developed and evaluated for reducing welding defects in CA6NM.
Publication date
Terms of use
NoteA CD-only volume
Linkhttp://www.programmaster.org/PM/PM.nsf/ApprovedAbstracts/404D3E791ABD35B585257AFD000F3965?OpenDocument
LanguageEnglish
Peer reviewedYes
NPARC number21276124
Export citationExport as RIS
Report a correctionReport a correction
Record identifier78e61e80-823d-4448-8233-0e63f39e6bf6
Record created2015-09-24
Record modified2019-02-14
Date modified:
Report a problem on this page