| Auteur | Rechercher : Zhang, Xinge1; Rechercher : Tsay, Ken1; Rechercher : Fahlman, Jason1; Rechercher : Qu, Wei1 |
|---|
| Affiliation | - Conseil national de recherches du Canada. Énergie, les mines et l'environnement
|
|---|
| Format | Texte, Article |
|---|
| Sujet | Zn morphology; pulsating deposition; zinc electrode; Zn–air battery |
|---|
| Résumé | The morphology of Zn deposit can be controlled by pulse deposition. Using defined pulse parameters (20 millisecond-on and 80 millisecond-off), the deposition current density was examined in 50–200 mA cm−2, in the electrolyte 9 M KOH + 5wt% ZnO, at room temperature (approximately 20°C) on a Zn plate. The obtained Zn morphology is a well-compact boulder microstructure below 100 mA cm−2. The coulombic efficiency of the deposition is close to 100%. The obtained Zn deposit shows over 90% packing density, with good adhesion to the Zn plate. A change in Zn morphology with deposition time is also observed. The compact boulder microstructure form in the 1 h deposition time becomes a granular spongy Zn after 5 h of deposition. |
|---|
| Date de publication | 2019-09-25 |
|---|
| Dans | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | 02c0668a-5fd6-4c7b-b474-d3174e72c309 |
|---|
| Enregistrement créé | 2021-09-03 |
|---|
| Enregistrement modifié | 2021-09-03 |
|---|