Room‐temperature aging of Narmco 5208 carbon‐epoxy prepreg. Part II: physical, mechanical, and nondestructive characterization

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1002/pc.750120311
AuteurRechercher : 1; Rechercher : 1; Rechercher : 1; Rechercher : 1; Rechercher : 1; Rechercher : ; Rechercher :
Affiliation
  1. Conseil national de recherches du Canada. Institut des matériaux industriels du CNRC
FormatTexte, Article
Résumé
Samples of Narmco Rigidite 5208/WC3000 carbon-epoxy composite prepreg were exposed to ambient temperature (22°C) and 50 percent relative humidity for different periods up to 66 days. The aging has a significant effect on prepreg physical properties such as tack, volatiles content, and gel time. A set of 4-ply laminates made from aged prepreg was subjected to tensile testing, ultrasonic inspection, and optothermal inspection. No relationship could be discerned between laminate properties and prepreg aging time. However, variations in panel homogeneity were observed, and these correlated with thermal diffusivity and tensile modulus measurements, but not with ultimate tensile strength or elongation. A set of 6-ply laminates was used to measure compressive properties, interlaminar shear strength, and physical properties. These panels also showed variations in porosity, again unrelated to aging, but in addition, the fiber/resin ratio was observed to decrease with aging time. Both factors were found to affect mechanical properties. The implications concerning the importance of monitoring the aging by physicochemical methods are discussed.
Date de publication
Maison d’éditionWiley
Society of Plastics Engineers
Dans
  • Polymer Composites 12, nº 3 (juin 1991) : 203–212.
Langueanglais
Publications évaluées par des pairsOui
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement0404dc1d-c644-4d25-a584-d7ed54784b84
Enregistrement créé2024-03-13
Enregistrement modifié2024-03-13
Date de modification :