| DOI | Trouver le DOI : https://doi.org/10.5006/1.3659505 |
|---|
| Auteur | Rechercher : Han, Y.; Rechercher : Gallant, D.1; Rechercher : Chen, X.-G. |
|---|
| Affiliation | - Conseil national de recherches du Canada
|
|---|
| Format | Texte, Article |
|---|
| Sujet | Electrochemical impedance; Galvanic coupling; Metal matrix composites; Potentiodynamics; Sulfate solutions; Aluminum; Boron; Boron carbide; Chlorine compounds; Corrosion; Corrosive effects; Electrochemical corrosion; Electrochemical impedance spectroscopy; Pitting; Polarization; Potentiodynamic polarization; Scanning electron microscopy; X ray photoelectron spectroscopy; Metallic matrix composites |
|---|
| Résumé | The corrosion behavior of Al-B4C (aluminum-boron carbide) metal matrix composites in a 0.5 M potassium sulfate (K2SO4) solution was investigated using electrochemical impedance spectroscopy and potentiodynamic polarization methods. Optical and scanning electron microscopes as well as profilometry were used to study the surface morphology of the material before and after corrosion. Moreover, infrared reflectionabsorption spectroscopy (IRRAS) and x-ray photoelectron spectroscopy (XPS) were used to identify the corrosion products. It was observed that SO4 2- species did not induce pitting of the AA1100 (UNS A91100)-16 vol% B4C. In contrast, it was found that the Al-B4C composite was highly susceptible to pitting attacks by chloride ions, especially at the Al/B4C interfaces. The B4C particles showed a cathodic character with respect to the peripheral matrix, and both the IRRAS and XPS results showed that bayerite (Al[OH]3) was the main corrosion product. © 2011, NACE International. |
|---|
| Date de publication | 2011 |
|---|
| Dans | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Numéro NPARC | 21271648 |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | 09def841-2549-4195-abb4-eeea9b2eaedc |
|---|
| Enregistrement créé | 2014-03-24 |
|---|
| Enregistrement modifié | 2020-04-21 |
|---|