Thermal stability of sulfur passivated InP(100)-(1×1)

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1063/1.112662
AuteurRechercher : ; Rechercher : ; Rechercher : ; Rechercher : 1; Rechercher : 1
Affiliation
  1. Conseil national de recherches du Canada. Institut des sciences des microstructures du CNRC
FormatTexte, Article
Sujetauger effect; evaporation; indium phosphides; leed; passivation; sem; stability; sulfur additions; surface reconstruction; thermal testing
Résumé
Auger electron spectroscopy, low-energy electron diffraction, thermal desorption spectroscopy, and scanning electron microscopy have been utilized to investigate the thermal stability of S-passivated InP(100). S-passivated InP(100) is shown to be thermally stable up to ~730 K, where S removal and sample evaporation begins. This evaporation results in the formation of a roughened, but clean, InP(100) surface, showing the characteristic (4×2) reconstruction.
Date de publication
Dans
  • Applied Physics Letters 65, nº 2 (11 juillet 1994) : 171–173.
Langueanglais
Numéro NPARC12329040
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement0ece4f5b-2600-436f-af74-34282f03f5a2
Enregistrement créé2009-09-10
Enregistrement modifié2020-04-27
Date de modification :