| DOI | Trouver le DOI : https://doi.org/10.1016/j.apsusc.2011.05.115 |
|---|
| Auteur | Rechercher : Li, X.1; Rechercher : Liu, X.1; Rechercher : Luan, B.L.1 |
|---|
| Affiliation | - Conseil national de recherches du Canada. Institut des matériaux industriels du CNRC
|
|---|
| Format | Texte, Article |
|---|
| Sujet | Coated sample; Low porosity; Pin-on-disk wear test; Plasma electrolytic oxidation; Potentiodynamic polarization tests; SEM analysis; Thick coatings; Wear properties; Wear volume loss; Alloys; Corrosion; Electrolysis; Electrolytes; Magnesium; Magnesium alloys; Oxidation; Wear resistance; X ray diffraction; Protective coatings |
|---|
| Résumé | Coatings with a thickness of 22-32 μm were formed on an AM60B magnesium alloy by plasma electrolytic oxidation (PEO) in electrolytes containing 12.0-24.0 g/l NaAlO2 and other additives. SEM analyses of the coated samples showed that the coatings were compact with relatively low porosity. X-ray diffraction revealed that the coatings consisted of mainly MgAl 2O4 and MgO phases. The relative amount of MgAl 2O4 in the coating increased with increasing NaAlO 2 concentration. The relatively compact and thick coatings provide good corrosion protection for magnesium, as indicated by the results of potentiodynamic polarization tests. In addition, the PEO treatment also significantly improved the wear resistance of the alloy. Pin-on-disk wear tests showed that the PEO treatment reduced the wear volume loss by a factor of 10. © 2011 Elsevier B.V. All rights reserved. |
|---|
| Date de publication | 2011 |
|---|
| Dans | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Numéro NPARC | 21271475 |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | 1cd1eae6-ab1e-417e-a803-ca97a9988771 |
|---|
| Enregistrement créé | 2014-03-24 |
|---|
| Enregistrement modifié | 2020-04-21 |
|---|