A new iron-rich intermetallic-Al m Fe phase in Al-4.6Cu-0.5Fe cast alloy

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1007/s11661-011-1004-5
AuteurRechercher : ; Rechercher : 1; Rechercher :
Affiliation
  1. Conseil national de recherches du Canada. Aérospatiale
FormatTexte, Article
Résumé
A new iron-rich intermetallic, Al m Fe, is observed, for the first time, in the important A206 (Al-4.6Cu-0.5Fe) cast alloy and identified using electron backscattered diffraction (EBSD) and a transmission electron microscope (TEM). Results show that Chinese script Al m Fe can precipitate as the dominant iron-rich intermetallic at high iron content (0.5 wt pct) and low cooling rate (0.2 K/s). EBSD and TEM results confirmed that Al m Fe has body-centered-tetragonal structure with an average m of approximately 4.2.
Date de publication
Dans
  • Metallurgical and Materials Transactions A 43, nº 4 (5 janvier 2012) : 1097–1101.
Langueanglais
Publications évaluées par des pairsOui
Identificateur1004
Numéro NPARC21268421
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement26e3bde7-bbd1-476f-a50a-ecd93a8e2ac0
Enregistrement créé2013-07-11
Enregistrement modifié2020-04-21
Date de modification :