Alternating current impedance: utility in evaluating phosphate coating, phosphorus-chromium rinse, and paint performance

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1021/bk-1986-0322.ch006
AuteurRechercher : 1; Rechercher : 1; Rechercher : 1
Affiliation
  1. Conseil national de recherches du Canada. Institut des matériaux industriels du CNRC
FormatTexte, Chapitre de livre
Résumé
Surface preparation methods are related to impedance behavior of painted aluminum-killed 1006 steel in a 3 weight percent sodium chloride solution. Variation of phosphating time, anodic phosphating, phosphochromic rinse, paint thickness, temperature of test solution and immersion time are studied using two different types of paints. For porous coatings, the beneficial effects of phospho-chromic rinse is confirmed. Decrease in coating resistance and increase in capacitance are observed with increasing time of immersion as well as with increasing test temperature. Progress in deterioration is indicated by the appearance of Warburg-type behavior. Good protection is obtained by phosphating for 5 minutes.
Date de publication
Maison d’éditionAmerican Chemical Society
Dans
  • Polymeric Materials for Corrosion Control : 58–76.
Série
  • ACS Symposium Series 322.
Langueanglais
Publications évaluées par des pairsOui
Numéro du CNRCCNRC 26584
NRC-IGM86-202-430
Numéro NPARC23003995
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement2db925d3-856f-4d60-8e54-c3e505f863a4
Enregistrement créé2018-09-12
Enregistrement modifié2020-06-10
Date de modification :