| DOI | Trouver le DOI : https://doi.org/10.1016/j.cclet.2013.11.051 |
|---|
| Auteur | Rechercher : Tang, H.-W.; Rechercher : Gao, N.; Rechercher : Chang, Z.-R.; Rechercher : Li, B.; Rechercher : Yuan, X.-Z.1; Rechercher : Wang, H.-J.1 |
|---|
| Affiliation | - Conseil national de recherches du Canada
|
|---|
| Format | Texte, Article |
|---|
| Résumé | Sub-micron-scaled sodium cobalt oxide (NaCo2O4) powders are prepared by a solid-state reaction method. Characterization using X-ray diffraction indicates that the synthesized NaCo2O4 has a hexagonal layered structure. The electrochemical performance of the NaCo2O4 electrodes is investigated using cyclic voltammetry and galvanostatic charge/discharge in NaOH solution. The results show that the specific capacitance of the NaCo2O4 electrode reaches 337 F/g over the potential range of 0.15-0.65 V at a mass normalized current of 50 mA/g. Moreover, NaCo2O4 exhibits very good stability and cycling performance as a supercapacitor material. © 2013 Zhao-Rong Chang. |
|---|
| Date de publication | 2013 |
|---|
| Dans | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Numéro NPARC | 21270966 |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | 2eb74432-cc6f-4ff5-9f1a-9cc88daecd84 |
|---|
| Enregistrement créé | 2014-02-18 |
|---|
| Enregistrement modifié | 2020-04-22 |
|---|