Porous Ni0.14Mn0.86O1.43 hollow microspheres as high-performing anodes for lithium-ion batteries

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1016/j.jpowsour.2015.05.021
AuteurRechercher : ; Rechercher : ; Rechercher : ; Rechercher : ; Rechercher : 1Identifiant ORCID : https://orcid.org/0000-0002-1823-2948; Rechercher : ; Rechercher : 1
Affiliation
  1. Conseil national de recherches du Canada. Énergie, les mines et l'environnement
FormatTexte, Article
Sujetlithium ion batteries; anode; Ni0.14Mn0.86O1.43; porous and hollow microspheres
Résumé
A uniformly dispersed bi-component nanocompotise of transition metal oxide (Mn2O3)/mixed transition metal oxide (NiMn2O4) with a porous and hollow microspheric sructure has been successfully prepared with a facile method based on the complexation between Ni2+ and NH3. The obtained nanocomposite of 0.29 Mn2O3/0.14 NiMn2O4, expressed as Ni0.14Mn0.86O1.43, with nanometer-sized building blocks exhibits a high reversible capacity of 615 mA h g−1, which is about 90% of theoretical value at the current density of 800 mA h g−1, and long lifespan with retained capacities of 553 and 408 mA h g−1 after 150 cycles at 200 and 800 mA g−1, respectively, as an anode material for lithium-ion batteries.
Date de publication
Dans
  • Journal of power sources 291 (septembre 2015) : 156–162.
Langueanglais
Publications évaluées par des pairsOui
Numéro NPARC21276020
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement3f612a50-523d-4bf5-9478-e0b8e0d3c5f5
Enregistrement créé2015-09-14
Enregistrement modifié2021-08-13
Date de modification :