Hydrogen diffusion in aluminum-killed low carbon steels

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1016/0257-8972(86)90082-4
AuteurRechercher : 1; Rechercher : 1; Rechercher : 1; Rechercher : ; Rechercher :
Affiliation
  1. Conseil national de recherches du Canada
FormatTexte, Article
Résumé
Hydrogen diffusion has been studied in aluminum-killed 1006 steel by the electrochemical technique of hydrogen permeation. Diffusion coefficients reproducible to within 10% have been obtained with the addition of thiourea in the cathodic compartment. The diffusion coefficient increases with increasing Al:N ratio. This phenomenon has been related to the anisotropy of the steel and to the grain size. On the basis of calculations proposed by Leblond and Dubois, the presence of irreversible traps is indicated in this type of steel. The irreversibly absorbed hydrogen concentration shows a tendency to increase with nitrogen content. Compared with aluminum-killed 1006 steel, decarburized rimmed steel shows a higher capacity for retaining irreversibly absorbed hydrogen.
Date de publication
Maison d’éditionElsevier
Dans
  • Surface & Coatings Technology 28, nº 3-4 : 225–237.
Langueanglais
Publications évaluées par des pairsOui
Numéro du CNRCCNRC 26232
NRC-IGM85-304-190
Numéro NPARC23004019
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement44f441ff-df40-49eb-9eb0-e829f899ae9b
Enregistrement créé2018-09-18
Enregistrement modifié2020-03-17
Date de modification :