Plastic deformation and fracture behavior of a Fe-modified Al3 Ti-base L12 intermetallic alloy

Par Conseil national de recherches du Canada

Téléchargement
  1. (PDF, 2.4 Mio)
DOITrouver le DOI : https://doi.org/10.1557/JMR.1991.0957
AuteurRechercher : ; Rechercher : ; Rechercher : ; Rechercher :
FormatTexte, Article
Sujetplastic deformation
Résumé
The microstructure of the ordered intermetallic alloy with a nominal composition of Al66Fe9Ti24 is nearly single-phase L12 structure, with a few second phase agglomerates at some grain corners. Room temperature compression tests showed that this material exhibits a plastic strain of about 11% at fracture. Final fracture of the compression specimens occured by a shear-off process along a surface oriented about 45 degrees to the compression axis. Fractographic analysis revealed that the fracture is transcrystalline and the fracture mode is mainly quasicleavage plus tearing. Transmission electron microscopy (TEM) was used to explore its deformation mechanisms. The dislocation density was low after homogenization, but is greatly increased during deformation. The deformation mode was found to be {110}{111} slip instead of twinning as in Al3Ti. The Α{110} superdislocations dissociated into two partials of Α/3(211)-type, bounding a superlattice intrinsic stacking fault (SISF) on the {111} slip plane.
Date de publication
Dans
  • Journal of Materials Research 6, nº 5 (mai 1991) : 957–963.
Langueanglais
Publications évaluées par des pairsOui
Publication du CNRC
Cette publication n’est pas du CNRC

Ce sont des publications qui ont été rédigées par un auteur du CNRC, mais avant que celui-ci soit employé du CNRC.

Numéro NPARC21276877
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement45bb1bc5-1c15-4ae0-b4fb-9ec1b62ba257
Enregistrement créé2015-10-30
Enregistrement modifié2020-06-04
Date de modification :