| DOI | Trouver le DOI : https://doi.org/10.1016/j.orgel.2015.07.006 |
|---|
| Auteur | Rechercher : Li, Zhao1; Rechercher : Ding, Jianfu1; Rechercher : Lefebvre, Jacques1; Rechercher : Malenfant, Patrick R. L.1 |
|---|
| Affiliation du nom | - Conseil national de recherches du Canada. Technologies de sécurité et de rupture
|
|---|
| Format | Texte, Article |
|---|
| Sujet | Amino acids; Carbon; Conjugated polymers; Interfaces (materials); Thin film transistors; Thin films; Yarn; Device performance; Different substrates; Dip-coating process; Interface modification; Network formation; Network morphology; Surface effect; Thin-film transistor (TFTs); Single-walled carbon nanotubes (SWCN) |
|---|
| Résumé | SWCNT network morphology and TFT performance of polyfluorene wrapped sc-SWCNT on different substrates is reported. The polymer/tube weight ratio and concentration impacts network formation and device performance. Hydrophilic SiO<inf>2</inf> surfaces show stronger adsorption compared to poly-l-lysine treated SiO<inf>2</inf>, which leads to more uniform and higher density networks. TFTs with mobility up to 38 cm2/Vs with <10% variability and on/off ratios on the order of 105 were obtained using an iterative dip-coating process. |
|---|
| Date de publication | 2015-11 |
|---|
| Dans | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Numéro NPARC | 21276983 |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | 4e6f3215-2ad9-4323-a110-78a6a2a64138 |
|---|
| Enregistrement créé | 2015-11-10 |
|---|
| Enregistrement modifié | 2020-04-22 |
|---|