| DOI | Trouver le DOI : https://doi.org/10.4028/www.scientific.net/MSF.783-786.2833 |
|---|
| Auteur | Rechercher : Wanjara, Priti1; Rechercher : Cao, Xinjin1 |
|---|
| Affiliation | - Conseil national de recherches du Canada. Aérospatiale
|
|---|
| Format | Texte, Article |
|---|
| Conférence | 8th International Conference on Processing and Manufacturing of Advanced Materials, THERMEC 2013, December 2-6, 2013, Las Vegas, NV |
|---|
| Sujet | Butt welding; Electric arc welding; Heat affected zone; 6061; Aluminum construction; Butt joints; Hardening precipitates; Hybrid laser-arc welding; Optimized process; Root reinforcement; Weld bead geometry; Aluminum alloys |
|---|
| Résumé | Hybrid laser-arc welding (HLAW) of butt joints in 3.18 mm thick aluminum alloy (AA) 6061-T6 sheets was investigated in the present study. Under optimized process conditions, high integrity welds with approximately 2% shrinkage and gas porosity were obtained. The weld bead geometry was determined to conform to the crown and root reinforcement specifications for welded aluminum construction - CSA W 59.2 M1191. Softening in the heat-affected zone (HAZ) and fusion zone (FZ) of the welds was observed, the former due to grain coarsening and the latter due to the dissolution of the hardening precipitates as well as the dilution from the application of the ER 5356 filler wire. Under optimized process conditions, the gap tolerance was determined to be 0.5 mm, beyond which the performance of the joints during bend testing was compromised. |
|---|
| Date de publication | 2014 |
|---|
| Dans | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Numéro NPARC | 21272152 |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | 4f2835ef-18fa-4a0b-ad3b-3e42cbda362c |
|---|
| Enregistrement créé | 2014-07-23 |
|---|
| Enregistrement modifié | 2020-04-22 |
|---|