| Sujet | Cathodes; Deposition; Diffusion; Diffusion coatings; Nickel; Solid solutions; Arc deposition; NbCr₂(HT) phase; NbNi₃ phase; Nickel chromium; Vacuum heat treatment; Heat treatment |
|---|
| Résumé | The formation of the inter-diffusion zone (IDZ) between NiCrAlY coating and Nb substrate during vacuum heat treatment was investigated. A NiCrAlY coating was applied on Nb substrate by cathode arc deposition. Vacuum heat treatments were carried out at 800°C, 900°Cand 1000°C for 2 h. SEM, EPMA, EDS and XRD were performed to analyze the microstructure of the IDZ and the results were interpreted using the 1002°C isothermal ternary Nb-Ni-Cr phase diagram. It was found that at 800°C the IDZ has a single NbNi₃ layer; at 900°C the IDZ consists of an outer NbNi₃ layer, a thin intermediate NbCr₂(HT) layer and an inner Nb₇Ni₆ layer; at 1000°C the IDZ has three well-developed layers: an outer NbNi₃ layer, an intermediate NbCr₂(HT) layer and an inner Nb₇Ni₆ layer. A small amount of Cr exists in both NbNi₃ and Nb₇Ni₆ phases as solid solution, and a large amount of Ni in NbCr₂(HT) phase as solid solution. |
|---|
| Date de publication | 2014-09-01 |
|---|
| Dans | |
|---|
| Traduction de | |
|---|
| Langue | japonais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Numéro NPARC | 21275469 |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | 5d04a9ed-206a-4ff3-a09e-647f6bf3ddd8 |
|---|
| Enregistrement créé | 2015-07-14 |
|---|
| Enregistrement modifié | 2023-02-20 |
|---|