| Auteur | Rechercher : Yuan, Xianxia; Rechercher : Li, Lin; Rechercher : Ma, Zhong; Rechercher : Yu, Xuebin; Rechercher : Wen, Xiufang; Rechercher : Ma, Zi-Feng; Rechercher : Zhang, Lei1Identifiant ORCID : https://orcid.org/0000-0002-1823-2948; Rechercher : Wilkinson, David P.; Rechercher : Zhang, Jiujun1 |
|---|
| Affiliation | - Conseil national de recherches du Canada. Énergie, les mines et l'environnement
|
|---|
| Format | Texte, Article |
|---|
| Résumé | A novel nanowire-structured polypyrrole-cobalt composite, PPy-CTAB-Co, is successfully synthesized with a surfactant of cetyltrimethylammounium bromide (CTAB). As an electro-catalyst towards oxygen reduction reaction (ORR) in alkaline media, this PPy-CTAB-Co demonstrates a superior ORR performance when compared to that of granular PPy-Co catalyst and also a much better durability than the commercial 20 wt% Pt/C catalyst. Physiochemical characterization indicates that the enhanced ORR performance of the nanowire PPy-CTAB-Co can be attributed to the high quantity of Co-pyridinic-N groups as ORR active sites and its large specific surface area which allows to expose more active sites for facilitating oxygen reduction reaction. It is expected this PPy-CTAB-Co would be a good candidate for alkaline fuel cell cathode catalyst. |
|---|
| Date de publication | 2016-02-10 |
|---|
| Dans | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Numéro NPARC | 21277487 |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | 610e7fef-abd8-476d-8310-e045635ebf3e |
|---|
| Enregistrement créé | 2016-03-09 |
|---|
| Enregistrement modifié | 2021-08-13 |
|---|