Mullite/alumina particulate composites by infiltration processing : III, mechanical properties

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1111/j.1151-2916.1991.tb06784.x
AuteurRechercher : ; Rechercher :
FormatTexte, Article
Résumé
The effect of incorporating mullite into alumina by an infiltration process on the mechanical properties was investigated. Data for Young's modulus, strength, and fracture toughness for various composite compositions were compared with those for the unreinforced matrix (alumina). Measurements of Young's modulus by a resonance technique showed that the addition of mullite decreased Young's modulus. Up to 14 vol%, these changes were close to those expected, but above this mullite content, the decrease was more dramatic and indicated specimen damage during processing. The addition of mullite led, in some cases, to increases of more than 60% in both the strength (biaxial flexure) and indentation fracture toughness. These increases have been attributed to the method of introducing mullite and the resulting residual compressive surface stresses. The strength of the indented composite bodies deviated from the ideal behavior, indicating the probability of R‐curve behavior in these materials.
Date de publication
Maison d’éditionWiley
Dans
  • Journal of the American Ceramic Society 74, nº 10 : 2453–2459.
NoteSupported by the National Research Council of Canada
Langueanglais
Publications évaluées par des pairsOui
Publication du CNRC
Cette publication n’est pas du CNRC

Ce sont des publications qui ont été rédigées par un auteur du CNRC, mais avant que celui-ci soit employé du CNRC.

Numéro du CNRCCNRC 33379
NRC-IMI91AP-20200-1253-G
Numéro NPARC23004669
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement6268fb15-bfca-495e-bbc0-a0a5df536d06
Enregistrement créé2018-12-07
Enregistrement modifié2020-03-17
Date de modification :