Plasma-sprayed semiconductor electrodes: photoelectrochemical properties of TiO₂

DOI	Trouver le DOI : https://doi.org/10.1149/1.2113629
Auteur	Rechercher : Parent, L.; Rechercher : Dodelet, J. P.; Rechercher : Ross, G. G.; Rechercher : Terreault, B.; Rechercher : Dallaire, S.¹
Affiliation	Conseil national de recherches Canada
Format	Texte, Article
Sujet	TiO₂; semiconductor; photoanode; plasma spray technique; photoelectrochemistry
Résumé	TiO₂ photoanodes have been prepared by the plasma spray technique on titanium, graphite, and alumina substrates. 25–30 μm thickcoatings display a good adhesion to the substrate and a highly textured surface. Dark and photoelectrochemical propertiesof the photoanodes have been measured in oxygen‐saturated solutions of NaOH at pH 13. It is shown that the performances of the electrodes are quite insensitive to the plasma power or to the TiO₂ powder granulation but are very sensitive to the purity of the spraying material, to the substrate, and also to a heat‐treatment(H₂ or Ar at 800°C followed by a rapid quenching in air). The maximum quantum yield is obtained at 300 nm for heat‐treated TiO₂ . It is about 40% on alumina and 70% on the titanium. The heat‐treatment affects the conductivity, σ, and the surface densityof hydroxyl groups, Noh , of the coatings. For heat‐treated TiO₂ , typical values are σ = 2.4(Ω cm)⁻¹ and Noh = 2.8 x 10¹⁶ cm⁻² . For untreated TiO₂ , typical values are σ = 30.6(Ωcm)⁻¹ and Noh + 2.1 X 10¹⁶ cm ⁻². The J‐V curves of heat‐treated TiO₂ sprayed on alumina extend anodically up to 9.5V (vs. SCE), where film breakdown occurs. For the same film sprayed on titanium and graphite, the anodic dark behavior is similarto that observed for the bare substrates. It is concluded that polycrystalline TiO₂ coatings, produced by the plasma spray technique, can display photoelectrochemical and dark characteristics similar to theones obtained with single‐crystal material.
Date de publication	1985-12-31
Maison d’édition	Electrochemical Society
Dans	Journal of The Electrochemical Society 132, nº 11 : 2590–2593.
Langue	anglais
Publications évaluées par des pairs	Oui
Numéro du CNRC	CNRC 26219 NRC-IGM85-301-166
Exporter la notice	Exporter en format RIS
Signaler une correction	Signaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement	6acdc306-7b56-4cc5-90c1-dc754bfa1d3e
Enregistrement créé	2019-03-26
Enregistrement modifié	2020-03-17

Détails de la page

Par :

Conseil national de recherches Canada

Date de modification :: 2026-04-20