| Téléchargement | - Voir le manuscrit accepté : Low polarization resistance of Ni-Cu-Ce oxide anode synthesized by coprecipitation with tetramethylammonium carbonate for intermediate temperature SOFC (PDF, 600 Kio)
|
|---|
| DOI | Trouver le DOI : https://doi.org/10.1016/j.matlet.2010.01.049 |
|---|
| Auteur | Rechercher : Oishi, Naoki1; Rechercher : Yoo, Yeong1 |
|---|
| Affiliation | - Conseil national de recherches du Canada. Institut de technologie des procédés chimiques et de l'environnement du CNRC
|
|---|
| Format | Texte, Article |
|---|
| Sujet | Solid oxide fuel cell; Anode; Coprecipitation; Tetramethylammonium carbonate; Polarization resistance |
|---|
| Résumé | With little deviation from the metal cation stoichiometry in a starting metal nitrate solution, Ni–Cu–Ce oxide powders for intermediate temperature SOFC anodes were synthesized by coprecipitation using tetramethylammonium carbonate and decomposition of coprecipitated metal carbonates. The synthesized oxide powder was found to have a high surface area. A 30% Ni–30% Cu–40% Ce anode fired at a low temperature of 900 °C on a Ce0.9Gd0.1O1.95 electrolyte provided low electrode polarization with an estimate of less than 0.1 Ω cm2 at temperatures over 600 °C on wet 50% H2 despite the Ni–Cu metallic phase in the anode was only 30% by volume. |
|---|
| Date de publication | 2010-01-21 |
|---|
| Dans | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Numéro du CNRC | NRCC 51933 |
|---|
| Numéro NPARC | 14814867 |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | 6eea2d82-e47d-4954-8810-7b2659925c26 |
|---|
| Enregistrement créé | 2010-03-30 |
|---|
| Enregistrement modifié | 2020-04-17 |
|---|