Sujet | Accelerated degradation tests; Air cathode; Alkaline conditions; Cathode catalyst; Electrochemical stabilities; Half cells; Initial mass; Mass activity; Oxygen reduction reaction; Peak power densities; Precious metal catalysts; Pt/C catalysts; Single cells; Zinc air battery; Degradation; Electrocatalysts; Electrolytic reduction; Oxygen; Precious metals; Stability; Testing; Zinc; Platinum alloys |
---|
Résumé | The electrochemical stability of non-precious FeCo-EDA and commercial Pt/C cathode catalysts for zinc air battery have been compared using accelerated degradation test (ADT) in alkaline condition. Outstanding oxygen reduction reaction (ORR) stability of the FeCo-EDA catalyst was observed compared with the commercial Pt/C catalyst. The FeCo-EDA catalyst retained 80% of the initial mass activity for ORR whereas the commercial Pt/C catalyst retained only 32% of the initial mass activity after ADT. Additionally, the FeCo-EDA catalyst exhibited a nearly three times higher mass activity compared to that of the commercial Pt/C catalyst after ADT. Furthermore, single cell test of the FeCo-EDA and Pt/C catalysts was performed where both catalysts exhibited pseudolinear behaviour in the 12-500 mA cm-2 range. In addition, 67% higher peak power density was observed from the FeCo-EDA catalyst compared with commercial Pt/C. Based on the half cell and single cell tests the non-precious FeCo-EDA catalyst is a very promising ORR electrocatalyst for zinc air battery. © 2010 Elsevier B.V. All rights reserved. |
---|
Date de publication | 2011 |
---|
Dans | |
---|
Langue | anglais |
---|
Publications évaluées par des pairs | Oui |
---|
Numéro NPARC | 21271554 |
---|
Exporter la notice | Exporter en format RIS |
---|
Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
---|
Identificateur de l’enregistrement | 72591348-e060-404c-b543-016bef10feb9 |
---|
Enregistrement créé | 2014-03-24 |
---|
Enregistrement modifié | 2020-04-21 |
---|