Permeability of oxygen and water vapor through polyethylene/polyamide films

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1002/pen.760241711
AuteurRechercher : ; Rechercher : ; Rechercher : 1
Affiliation
  1. Conseil national de recherches du Canada
FormatTexte, Article
Résumé
Oxygen and water vapor permeability studies were carried out on binary polyethylene/polyamide immiscible blends incorporating three polyethylene resins (LDPE, LLDPE, and HDsPE), and three polyamide resins (PA‐6, PA‐6,6, and modified PA‐6,6m). It was found that the incorporation of PA into PE reduces the oxygen permeability while water vapor permeability is increased. In the range of 0 to 30 weight percent of PA, the oxygen permeability of PE was reduced by a factor of 2.8 to 3.6. Maximum water vapor permeabilities increased: for HDPE by a factor of about 2.6 to 3.1 and for LDPE and LLDPE blends by about 1.6.
Date de publication
Maison d’éditionWiley
Dans
  • Polymer Engineering and Science 24, nº 17 : 1337–1347.
Langueanglais
Publications évaluées par des pairsOui
Numéro du CNRCCNRC 22999
NRC-IGM 84-102-112
Numéro NPARC23004036
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement7abf8e52-6ee1-4b0e-ae1c-78d7d98c24c0
Enregistrement créé2018-09-18
Enregistrement modifié2020-03-13
Date de modification :