Mullite alumina particulate composites by infiltration processing : II, infiltration and characterization

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1111/j.1151-2916.1990.tb04266.x
AuteurRechercher : ; Rechercher :
FormatTexte, Article
Résumé
Mullite/alumina composites were fabricated by infiltrating porous alumina preforms with a hydrolyzed ethyl silicate sol. Evidence is presented which suggests that initial infiltration occurred without complete filling of the porosity by the sol. Multiple infiltrations were used to increase the amount of SiO₂ introduced but led to blockage of the pores in the surface of the preform. Sintered bodies had concentration gradients, SiO₂ decreasing from the surface inward. Although mullite limited grain growth in alumina, in partially modified bodies large grains (>1 mm) with a preferred orientation were observed at the interface between the two zones
Date de publication
Maison d’éditionWiley
Dans
  • Journal of the American Ceramic Society 73, nº 12 : 3611–3616.
Langueanglais
Publications évaluées par des pairsOui
Publication du CNRC
Cette publication n’est pas du CNRC

Ce sont des publications qui ont été rédigées par un auteur du CNRC, mais avant que celui-ci soit employé du CNRC.

Numéro du CNRCCNRC 33349
NRC-IMI91AP-20200-1207G
Numéro NPARC23004500
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement803a0d69-a872-4f8c-b696-3eabf48dfbed
Enregistrement créé2018-11-09
Enregistrement modifié2020-03-17
Date de modification :