Téléchargement | - Voir le manuscrit accepté : Preparation and DMFC performance of a sulfophenylated poly(arylene ether ketone) polymer electrolyte membrane (PDF, 858 Kio)
|
---|
DOI | Trouver le DOI : https://doi.org/10.1016/j.electacta.2010.02.014 |
---|
Auteur | Rechercher : Liu, Baijun; Rechercher : Hu, Wei; Rechercher : Kim, Yu Seung; Rechercher : Robertson, Gilles P.1; Rechercher : Jiang, Zhenhua; Rechercher : Guiver, Michael D.1 |
---|
Affiliation | - Conseil national de recherches du Canada. Institut de technologie des procédés chimiques et de l'environnement du CNRC
|
---|
Format | Texte, Article |
---|
Sujet | Poly(aryl ether ketone)s; Polymer electrolyte membrane; Fuel cells; Membrane electrode assemblies; Direct methanol fuel cells |
---|
Résumé | A sulfonated poly(aryl ether ether ketone ketone) (PEEKK) having a well-defined rigid homopolymer-like chemical structure was synthesized from a readily prepared PEEKK by post-sulfonation with concentrated sulfuric acid at room temperature within several hours. The polymer electrolyte membrane (PEM) cast from the resulting polymer exhibited an excellent combination of thermal resistance, oxidative and dimensional stability, low methanol fuel permeability and high proton conductivity. Furthermore, membrane electrode assemblies (MEAs) were successfully fabricated and good direct methanol fuel cell (DMFC) performance was observed. At 2M MeOH feed, the current density at 0.5V reached 165 mA/cm, which outperformed our reported similarly structured analogues and MEAs derived from comparative Nafion® membranes. |
---|
Date de publication | 2010 |
---|
Dans | |
---|
Langue | anglais |
---|
Publications évaluées par des pairs | Oui |
---|
Numéro du CNRC | NRCC 51939 |
---|
Numéro NPARC | 16020205 |
---|
Exporter la notice | Exporter en format RIS |
---|
Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
---|
Identificateur de l’enregistrement | 82ecb104-462b-4212-8b65-8436ac29cdc4 |
---|
Enregistrement créé | 2010-09-02 |
---|
Enregistrement modifié | 2020-04-17 |
---|