| DOI | Trouver le DOI : https://doi.org/10.1117/12.2252248 |
|---|
| Auteur | Rechercher : Sinar, Dogan; Rechercher : Knopf, George K.; Rechercher : Nikumb, Suwas1 |
|---|
| Éditeur | Rechercher : Tabor, Christopher E.; Rechercher : Kajzar, François; Rechercher : Kaino, Toshikuni; Rechercher : Koike, Yasuhiro |
|---|
| Affiliation du nom | - Conseil national de recherches du Canada. Automobile et les transports de surface
|
|---|
| Format | Texte, Article |
|---|
| Conférence | SPIE OPTO, 28 January 2017, San Francisco, California, United States |
|---|
| Résumé | Optically transparent electrodes (OTEs) are used for bioelectronics, touch screens, visual displays, and photovoltaic cells. Although the conductive coating for these electrodes is often composed of indium tin oxide (ITO), indium is a very expensive material and thin ITO films are relatively brittle compared to conductive polymer or graphene thin films. An alternative highly conductive optically transparent thin film based on a graphene (G) and silver-nanoprism (AgNP) dispersion is introduced in this paper. The aqueous G ink is first synthesized using carboxymethyl cellulose (CMC) as a stabilizing agent. Silver (Ag) nanoprisms are then prepared separately by a simple thermal process which involves the reduction of silver nitrate by sodium borohydride. These Ag nanoprisms are only a few nanometers thick but have relatively large surface areas (>1000 nm2). As a consequence, the nanoprisms provide more efficient injection of free carriers to the G layer. The concentrated G-AgNP dispersions are then deposited on optically transparent glass and polyimide substrates using an inkjet printer with a HP6602A print head. After printing, these optically thin films can be thermally treated to further increase electrical conductivity. Thermal treatment decomposes CMC which frees elemental carbon from polymer chain and, simultaneously, causes the film to become hydrophobic. Preliminary experiments demonstrate that the G-AgNP films on glass substrates exhibit high conductivity at 70% transparency (550 nm). Additional tests on the Gr-AgNP thin films printed on polymide substrates show mechanical stability under bending with minimal reduction in electrical conductivity or optical transparency. |
|---|
| Date de publication | 2017-02-16 |
|---|
| Maison d’édition | Society of Photo-optical Instrumentation Engineers |
|---|
| Dans | |
|---|
| Série | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Numéro NPARC | 23003089 |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | 84da1bb1-8312-4778-ad00-f5c9faf8ccbd |
|---|
| Enregistrement créé | 2018-04-19 |
|---|
| Enregistrement modifié | 2020-03-16 |
|---|