Temperature and field dependence of resistivities and anisotropy of layered manganites La₂₋₂ₓSr₁₊₂ₓMn₂O₇

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1016/S0921-4534(00)00695-X
AuteurRechercher : ; Rechercher : ; Rechercher : ; Rechercher :
FormatTexte, Article
Résumé
In-plane ϱab and out-of-plane ϱc resistivities of La1.2Sr1.8Mn2O7 and LaSr2Mn2O7 have been measured by a multiterminal technique. We focus on the effects that magnetic and charge ordering transitions have on the anisotropy σab/σc which reflects the ratio of the phase coherence lengths in the respective directions. Both resistivities of La1.2Sr1.8Mn2O7 decrease dramatically below the Curie temperature TC ≈ 135 K. Anisotropy changes with temperature nonmonotonically and displays a peak close to TC. In LaSr2Mn2O7, ϱc and ϱab display a broad peak close to the paramagnetic-antiferromagnetic transition temperature TN ≈ 165 K. The anisotropy exhibits an even more complex behavior than in La1.2Sr1.8Mn2O7, displaying a maximum at the charge ordering temperature and a minimum at TN.
Date de publication
Dans
  • Physica C: Superconductivity 341-348, nº 2 (novembre 2000) : 791–792.
Publication du CNRC
Cette publication n’est pas du CNRC

Ce sont des publications qui ont été rédigées par un auteur du CNRC, mais avant que celui-ci soit employé du CNRC.

Numéro NPARC12329142
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement85004517-f2e4-4786-a4ff-f9694e95a912
Enregistrement créé2009-09-10
Enregistrement modifié2020-03-26
Date de modification :