Téléchargement | - Voir le manuscrit accepté : Mechanical properties of porous metastable beta Ti-Nb-Zr alloys for biomedical applications (PDF, 3.2 Mio)
|
---|
DOI | Trouver le DOI : https://doi.org/10.1016/j.jallcom.2011.12.157 |
---|
Auteur | Rechercher : Braïlovski, V.; Rechercher : Prokoshkin, S.; Rechercher : Gauthier, M.1; Rechercher : Inaekyan, K.; Rechercher : Dubinskiy, S. |
---|
Affiliation | - Conseil national de recherches du Canada. Institut des matériaux industriels du CNRC
|
---|
Format | Texte, Article |
---|
Conférence | ICOMAT 2011: International Conference on Martensitic Transformations, September 4-9, 2011, Osaka, Japan, 2011-09-04 |
---|
Sujet | Metals and alloys; Powder metallurgy; Sintering; Mechanical properties; Shape memory |
---|
Résumé | For this study, Ti–(20–22)Nb–(5–6)Zr (at percent) ingots were manufactured by vacuum and argon arc melting. The obtained ingots were divided into two batches: the first subjected to cold rolling (CR) from 30 to 85 percent of thickness reduction, and subsequent annealing in the 450–600 °C temperature range (1 h). Regardless of the CR intensity, Ti–Nb–Zr samples subjected to 600 °C annealing showed the highest fatigue resistance during room-temperature cumulative cycling due to the stress-induced martensitic transformation occurring in the polygonized dislocation substructure (average subgrain size ∼ 100 nm). The second batch was atomized to produce 100-μm-size powders in order to manufacture open-cell porous material (cell size vary from 136 to 561 μm) of 46 percent porosity by means of powder metallurgy using a polymer-based foaming process. Tensile, compression and bending testing were performed at RT on foam samples annealed at 450–600 °C (1 h). Results indicated that Young's modulus of Ti–Nb–Zr foams significantly decreases as compared to the as-sintered material: when annealing temperature increases from 450 to 600 °C, Young's modulus decreases from 10 ± 2 GPa to 6 ± 1 GPa. Under the same testing conditions, Ti-CP foams produced by the same technology and having similar porosity remain fairly insensible to post-sintering annealing. |
---|
Date de publication | 2012-02-06 |
---|
Dans | |
---|
Langue | anglais |
---|
Publications évaluées par des pairs | Oui |
---|
Numéro du CNRC | NRCC 54387 |
---|
Numéro NPARC | 19262898 |
---|
Exporter la notice | Exporter en format RIS |
---|
Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
---|
Identificateur de l’enregistrement | 8e4a22b1-1d73-4f94-98b0-d9e90fa30567 |
---|
Enregistrement créé | 2012-01-13 |
---|
Enregistrement modifié | 2020-04-21 |
---|