Auteur | Rechercher : Huang, M. H.; Rechercher : Liao, M.1; Rechercher : Szpunar, J. A. |
---|
Affiliation | - Conseil national de recherches du Canada. Institut de recherche aérospatiale du CNRC
|
---|
Format | Texte, Article |
---|
Conférence | 12th International Conference on Fracture 2009, ICF-12, July 12-17, 2009, Ottawa, ON, Canada |
---|
Résumé | Under a tension-compression loading condition applied with the frequency of 10Hz and stress ratio of 0.1, the fatigue behavior of the notched aluminum 7050-T7452 coupons was studied using scanning electron microscope (SEM), and SEM-based automated electron back-scatter diffraction (EBSD) that generates images of orientation of grains. The grain micro structure was determined with optical microscope (OM) by employing the lineal intercept method. OM observation demonstrates that the alloy is having a deformation band-based microstructure. The fatigue crack nucleates at grains with high angle (>15 degrees) misorientation in the area characterized by a weak texture and propagates transgranularly. |
---|
Date de publication | 2009 |
---|
Maison d’édition | Curran Associates |
---|
Dans | |
---|
Langue | anglais |
---|
Publications évaluées par des pairs | Oui |
---|
Numéro NPARC | 23004855 |
---|
Exporter la notice | Exporter en format RIS |
---|
Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
---|
Identificateur de l’enregistrement | 9cc9f6c1-717f-4de1-a3c5-d1d0793185da |
---|
Enregistrement créé | 2019-01-04 |
---|
Enregistrement modifié | 2020-04-16 |
---|