Study of spherulites in a semi-crystalline polymer using acoustic microscopy

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1557/PROC-142-253
AuteurRechercher : 1; Rechercher : 1; Rechercher : 1; Rechercher : 1; Rechercher : 1; Rechercher : 1
Affiliation
  1. Conseil national de recherches du Canada
FormatTexte, Article
Résumé
The local elastic properties of a semi-crystalline polymer (isotactic polypropylene) have been investigated with the use of scanning acoustic microscopy (SAM) techniques. The operating frequency was 775 MHz and the temperatures ranged between 25 and 60°C. A new and effective signal processing method was developed to process the material signature V(z) curve. This method avoids complicated calibration procedures involved with operating the SAM lens at different temperatures. Longitudinal velocities VL(α) and VL(β) in individual α and β-type spherulites of isothermally crystalized samples have been measured. Acoustic velocity of a quenched sample was also obtained. It was found that vL(α) and VL(β) were nearly equal but the acoustic impedances of α and β-spherulites were unexpectedly very different.
Date de publication
Maison d’éditionCambridge University Press
Materials Research Society
Dans
  • MRS Proceedings 142, 253 (1988).
Langueanglais
Publications évaluées par des pairsOui
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement9cef13a5-f6e2-4379-9a3b-f8088f293b77
Enregistrement créé2024-03-19
Enregistrement modifié2024-03-19
Date de modification :