| Téléchargement | - Voir la version finale : A room temperature process for forming highly conductive features (PDF, 598 Kio)
|
|---|
| DOI | Trouver le DOI : https://doi.org/10.4224/23000709 |
|---|
| Auteur | Rechercher : Zhang, Zhiyi1; Rechercher : Tao, Ye1; Rechercher : Fukutani, Hiroshi1; Rechercher : Xiao, Gaozhi1 |
|---|
| Affiliation | - Conseil national de recherches du Canada. Technologies de l'information et des communications
|
|---|
| Format | Texte, Allocution |
|---|
| Conférence | CPES2016: Printable, Flexible, Wearable Electronics Symposium, April 19-20 2016, Sheridan College, Oakville, ON, Canada |
|---|
| Résumé | A process was developed to deposit highly conductive features on plastic films and papers. In this process, a reactive silver ink, which contains a weak reducing agent and is stable at room temperature, is directly cast or printed on a pre-coated substrate at room temperature. The strong reducing agent coated on the substrate instantly reacts with the ink on its surface and cause the rapid silver deposition locally. As the heat generated from the reaction is quickly transferred to the upper part of the ink, it initiates silver reduction reaction in the section, resulting in the continuous silver build up from the surface. Silver features with a conductivity almost the same as that of bulk silver and a thickness of up to 1 micrometer can be obtained from this bottom-up silver reduction and thus silver growth process. The whole reduction process happens at room temperature within minutes without any external energy applied. |
|---|
| Date de publication | 2016-04-01 |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Non |
|---|
| Numéro NPARC | 23000709 |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | ac6adcf4-a08d-406e-bd96-6a8e87549753 |
|---|
| Enregistrement créé | 2016-08-31 |
|---|
| Enregistrement modifié | 2020-06-02 |
|---|