| Auteur | Rechercher : Palardy, G.; Rechercher : Trudel-Boucher, D.1; Rechercher : Hubert, P. |
|---|
| Affiliation | - Conseil national de recherches du Canada. Institut des matériaux industriels du CNRC
|
|---|
| Format | Texte, Article |
|---|
| Conférence | 24th Annual Technical Conference of the American Society for Composites 2009 and 1st Joint Canadian-American Technical Conference on Composites, September 15-17, 2009, Newark, DE; USA |
|---|
| Résumé | The main objective of this research is to develop a processing map to determine the optimal nanotube content leading to the maximum elastic modulus according to the allowable viscosity limit in melt spinning. In this work, multi-walled carbon nanotubes (MWNT) and polyamide 12 (Rilsan® PA 12) were studied. The characterization of PA 12 with MWNT contents of 0 wt%, 0.1 wt%, 0.5 wt%, 1.0 wt%, 2.0 wt% and 5.0 wt% was performed through differential calorimetry (DSC) and thermo-gravimetric analysis (TGA). Scanning electron microscopy (SEM) was used to assess the dispersion state of the nanotubes and relate those observations to the characterization results. The shear viscosity was investigated to identify optimal values for the production of fibres by melt spinning. MWNT contents below 5.0 wt% were selected to produce fibres according to the preliminary viscosity measurements, but further investigation of elongational and capillary viscosity will be needed. |
|---|
| Date de publication | 2010 |
|---|
| Maison d’édition | Current Associates |
|---|
| Dans | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Numéro NPARC | 23004700 |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | b020fea9-95b3-434d-b18a-e52dcb903b6f |
|---|
| Enregistrement créé | 2018-12-11 |
|---|
| Enregistrement modifié | 2020-04-17 |
|---|