| Résumé | A series of carbon supported cobalt-polypyrrole-4-toluenesulfinic acid have been pyrolyzed in an argon atmosphere at 800 C, then structurally characterized and electrochemically evaluated as oxygen reduction reaction (ORR) catalysts in aqueous 0.5 M sulfuric acid. The structures are cobalt bonded to nitrogen species (Co-Nx) along with metallic cobalt and cobalt oxide. When the cobalt loading in the compound is less than 1.0 wt%, the predominate form is Co-Nx, when the loading is higher than 1.0 wt%, metallic Co and Co oxide particles co-exist with the Co-Nx compound. At a Co loading of ∼1.0 wt%, the catalyst gives the best ORR activity. Both metallic Co and Co oxide are not active for catalyzing ORR, and block the catalytically active Co-Nx species from the surface and reduce the catalytic activity since the diffusion limiting current density on a rotating disk electrode (RDE) increases when the electrode blocking agents are washed away with acid. |
|---|