| Téléchargement | - Voir le manuscrit accepté : Solidification analysis of Al-Si alloy using in-situ neutron diffraction (PDF, 1.5 Mio)
|
|---|
| Auteur | Rechercher : Kasprzak, W.; Rechercher : Sediako, D.1; Rechercher : Sahoo, M.; Rechercher : Walker, M.; Rechercher : Swainson, I.1 |
|---|
| Éditeur | Rechercher : Gallienne, D.; Rechercher : Bilodeau, M. |
|---|
| Affiliation | - Conseil national de recherches du Canada. Centre canadien de faisceaux de neutrons du CNRC
|
|---|
| Format | Texte, Article |
|---|
| Conférence | COM 2010 49th Conference of Metallurgists, October 3-6, 2010, Vancouver, British Columbia |
|---|
| Résumé | In-situ neutron diffraction and thermal analysis techniques were used to evaluate the kinetics of the non-equilibrium solidification process of a hypereutectic Al-Si alloy using NRU nuclear reactor in Chalk River, ON and HFIR reactor in Oak Ridge National Lab, TN. Neutron diffraction patterns were collected in the stepwise mode during solidification between 740 and 400 degrees C. The variation of intensity of the diffraction peaks was analysed and compared with the results of a conventional cooling curve analysis. it was shown that neutron diffraction offers potential for high resolution liquid and semi-solid microstructure analysis and can be used for novel studies on grain refining, eutectic modification, etc. |
|---|
| Date de publication | 2010-10-01 |
|---|
| Dans | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Numéro NPARC | 16959080 |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | b4dce98f-1ffe-4a2b-9a50-ecb515ed4715 |
|---|
| Enregistrement créé | 2011-03-03 |
|---|
| Enregistrement modifié | 2020-04-17 |
|---|