| DOI | Trouver le DOI : https://doi.org/10.1063/1.117050 |
|---|
| Auteur | Rechercher : Schmuki, P.; Rechercher : Lockwood, David1; Rechercher : Labbe, H.; Rechercher : Fraser, Jeffrey1 |
|---|
| Affiliation | - Conseil national de recherches Canada. Institut des sciences des microstructures du CNRC
|
|---|
| Format | Texte, Article |
|---|
| Sujet | ELECTROCHEMISTRY; GALLIUM ARSENIDES; N - TYPE CONDUCTORS; PHOTOLUMINESCENCE; POROUS MATERIALS; SEM |
|---|
| Résumé | Porous GaAs was formed electrochemically on n-type GaAs(100) in a 0.1 M HCl electrolyte. Scanning electron microscopy revealed feature sizes of the porous structure in the micrometer to nanometer range. The optical properties of the porous material were characterized by photoluminescence (PL) measurements at 295 K. Compared with untreated GaAs, a shift down of the ``infrared'' PL maximum to ~ 840 nm can be observed. An additional ``green'' PL peak occurs at ~ 540 nm that in some samples is readily visible to the naked eye. The ``green'' and the ``infrared'' PL are ascribed to quantum confinement effects in GaAs nano- and microcrystallites, respectively. |
|---|
| Date de publication | 1996 |
|---|
| Dans | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Numéro NPARC | 12336512 |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | b57e9c71-1e65-450e-90c2-5e68999b0adc |
|---|
| Enregistrement créé | 2009-09-10 |
|---|
| Enregistrement modifié | 2023-05-10 |
|---|