Nanostructured and conventional Cr₂O₃, TiO₂, and TiO₂-Cr₂O₃ thermal-sprayed coatings for metal-seated ball valve applications in hydrometallurgy

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1007/s11666-016-0405-9
AuteurRechercher : ; Rechercher : ; Rechercher : ; Rechercher : 1; Rechercher : 1; Rechercher : ; Rechercher :
Affiliation du nom
  1. Conseil national de recherches du Canada. Automobile et les transports de surface
FormatTexte, Article
Sujetair plasma spraying (APS); ceramic coating; galling; high-pressure acid leaching (HPAL); pressure oxidation (POx); tribomechanical properties
Résumé
A detailed characterization project was undertaken by Velan, an international industrial valve designer and manufacturer, in collaboration with the National Research Council of Canada, Boucherville, and Polytechnique Montréal. The purpose was to assess the mechanical and tribological resistances of promising ceramic coatings for hydrometallurgy applications, including a novel n-TiO₂-Cr₂O₃ blend. Hardness and shear strength were determined using microhardness indentation testers and universal tensile testing equipment. Wear resistance of the coatings under sliding wear, abrasion, and galling conditions were measured by standard pin-on-disk tests, abrasion tests, and custom-designed galling tests. The main result is that the synergy between Cr₂O₃ and n-TiO₂ produced abrasion performance exceeding that of these materials alone. Also, an optimized balance between the hard and brittle Cr₂O₃ phases and the soft and ductile n-TiO₂ phases resulted in higher abrasion, sliding, and galling resistance. The novel n-TiO₂-Cr₂O₃ blend is therefore considered as a promising evolution of the current TiO₂-Cr₂2O₃3 blend.
Date de publication
Maison d’éditionSpringer International Publishing
EmplacementNew York, NY, USA
Dans
  • Journal of Thermal Spray Technology 25, nº 5 (7 avril 2016) : 1068–1078.
Langueanglais
Publications évaluées par des pairsOui
Identificateur405
Numéro du CNRCNRC-AST-BOU-0005
Numéro NPARC23000307
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrementc39801f7-e6b7-4724-aed4-006b1884b66e
Enregistrement créé2016-07-06
Enregistrement modifié2020-08-31
Signaler un problème ou une erreur sur cette page
Date de modification :