HVOF Coating case study for power plant process control ball valve application

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1007/s11666-013-9978-8
AuteurRechercher : ; Rechercher : ; Rechercher : 1; Rechercher : ; Rechercher :
Affiliation
  1. Conseil national de recherches du Canada
FormatTexte, Article
SujetCarbide precipitation; Chromium carbide; Cohesive failures; Failure mechanism; Power plant process; Self-fluxing alloys; Supercritical steam; Temperature variation; Carbides; Chromate coatings; Cracks; Decarburization; Failure (mechanical); High temperature applications; Power plants; HVOF thermal spraying
Résumé
This case study is the result of an investigation on HVOF 80/20 Cr 3C2-NiCr coating failure of on-off metal-seated ball valve (MSBV) used in supercritical steam lines in a power plant and solution. HVOF 80/20 Cr3C2-NiCr coating is used to protect thousands of MSBVs without incident. However, in this case, the valves are challenged with exposure to rapid high-pressure and -temperature variations resulting in a unique situation where the coating experiences cracking and cohesive failure. It was found that carbide precipitation is a major factor causing embrittlement of the coating. Once the coating toughness and ductility is reduced, thermal, mechanical, and residual stresses can initiate and propagate cracks more easily, causing coating failure when exposed to thermal shock. To alleviate the above mentioned issues, possible coating alternatives were then evaluated. © 2013 ASM International.
Date de publication
Dans
  • Journal of Thermal Spray Technology 22, nº 7 (2013) : 1184–1192.
Langueanglais
Publications évaluées par des pairsOui
Numéro NPARC21270623
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrementcaacd262-21ec-4b9c-9d07-706c663dc7d4
Enregistrement créé2014-02-17
Enregistrement modifié2020-04-22
Date de modification :