| Téléchargement | - Voir le manuscrit accepté : Sintering of 17-4PH stainless steel feedstock for metal injection molding (PDF, 1008 Kio)
|
|---|
| DOI | Trouver le DOI : https://doi.org/10.1016/j.matlet.2008.03.027 |
|---|
| Auteur | Rechercher : Ye, Hezhou; Rechercher : Liu, Xing Yang1; Rechercher : Hong, Hanping |
|---|
| Affiliation | - Conseil national de recherches du Canada. Institut des matériaux industriels du CNRC
|
|---|
| Format | Texte, Article |
|---|
| Sujet | sintering; powder technology; 17-4PH; metal injection molding |
|---|
| Résumé | The sintering behavior of 17-4PH stainless steel feedstock for metal injection molding was investigated in the temperature range of 650–1050 °C. Effects of sintering conditions, such as sintering temperature and sintering atmosphere, were examined. Results showed that when sintered in the hydrogen/nitrogen atmosphere, the 17-4PH feedstock was oxidized over the temperature range of investigation. The degree of oxidization increased with the sintering temperature. The main oxidization product was Cr2O3 as revealed by X-ray diffraction and composition analysis. The oxidation can be avoided by sintering in vacuum or argon atmosphere. |
|---|
| Date de publication | 2008-03-18 |
|---|
| Maison d’édition | Elsevier |
|---|
| Dans | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Numéro du CNRC | NRCC 49141 |
|---|
| Numéro NPARC | 21274317 |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | d4887db6-2d2d-4572-8581-7435fdd5da1b |
|---|
| Enregistrement créé | 2015-03-09 |
|---|
| Enregistrement modifié | 2020-09-08 |
|---|