Microstructure and tensile properties of Ti6Al4V/AM60B magnesium matrix composite

Par Conseil national de recherches du Canada

Téléchargement
  1. (PDF, 1.9 Mio)
DOITrouver le DOI : https://doi.org/10.1016/j.jallcom.2005.04.175
AuteurRechercher : 1; Rechercher : 1
Affiliation
  1. Conseil national de recherches du Canada. Institut des matériaux industriels du CNRC
FormatTexte, Article
Sujetmetal matrix composite; intermetallics; casting; segregation; tensile properties
Résumé
The low density of magnesium alloys makes them attractive for aerospace and automotive applications. In order to further improve the high temperature strength of the magnesium alloys, Ti6Al4V particles were added to an AM60B magnesium alloy to form a composite through melting and hot isostatic pressing. Increasing the Ti6Al4V content from 0 to 5 vol.%, however, produced no beneficial effect on tensile strengths at room temperature, but reduced the ductility. The pores existing between the matrix and Ti6Al4V particles in the as cast conditions, along with the segregation of Mn5Al8 intermetallic particles at the Ti6Al4V/matrix interface are believed to be responsible for the changes in mechanical properties.
Date de publication
Dans
  • Journal of Alloys and Compounds 402, nº 1-2 (14 juillet 2005) : 162–169.
Langueanglais
Publications évaluées par des pairsOui
Numéro NPARC21272509
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrementd86276f1-fa98-41ee-b9df-63b19a0c728a
Enregistrement créé2014-12-01
Enregistrement modifié2020-06-04
Date de modification :