Intermetallic phases in Al-Si based cast alloys: New perspective

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1179/1743133613Y.0000000083
AuteurRechercher : 1; Rechercher : ; Rechercher : ; Rechercher : ; Rechercher : 2
Affiliation
  1. Conseil national de recherches du Canada. Automobile et les transports de surface
  2. Conseil national de recherches du Canada
FormatTexte, Article
SujetCast alloys; Chemical compositions; Electron probe microanalyser; Equilibrium conditions; Intermetallic phasis; Q-phase; Sr modification; Aluminum; Intermetallics; Iron alloys; Manganese; Silicon; X ray spectroscopy; Silicon alloys
Résumé
The present work was performed on experimental Al-Si near eutectic cast alloys, with different additives mainly Fe, Mg, Mn, Cr, Sr and P. The alloys were cooled at 0·8°C s-1, very close to equilibrium conditions. Precipitated phases, primarily Fe, Cu, Mg and Sr based intermetallics, were examined. Although the phases reported in the present work were documented previously, the range of chemical composition of each phase was confirmed using an electron probe microanalyser equipped with wavelength dispersive spectroscopy and electron dispersive X-ray spectroscopy facilities.
Date de publication
Dans
  • International Journal of Cast Metals Research 27, nº 2 (2014) : 107–114.
Langueanglais
Publications évaluées par des pairsOui
Numéro NPARC21275492
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrementdede944a-6c03-41b1-8dcb-1cbe03a09e06
Enregistrement créé2015-07-14
Enregistrement modifié2020-04-22
Date de modification :