| Résumé | The effects of aging on the ballistic characteristics of monolithic polycarbonate were studied.
The program was carried out in two parts. Part I compared the decrease in bullet velocity after penetration of new to aged polycarbonate panels, and Part II compared the behaviour of new to aged panels where penetration does not occur.
No appreciable difference was noted in residual bullet velocity between those bullets which penetrated the different panels. In assessing bu1let resistance through non-penetration, no significant change was observed due to age degradation of the polycarbonate.
It was noted however, that both the artificially aged and naturally aged specimens behaved somewhat unpredictably and both showed signs of being susceptible to the initiation of fractures upon bullet impact. |
|---|
| Date de publication | 1982-03-17 |
|---|
| Maison d’édition | National Research Council of Canada. National Aeronautical Establishment |
|---|
| Série | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Non |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | e7628fe2-753e-4568-9be4-930399ddc9d4 |
|---|
| Enregistrement créé | 2022-01-13 |
|---|
| Enregistrement modifié | 2023-01-17 |
|---|