Téléchargement | - Voir le manuscrit accepté : Extrusion Foaming of Semi-Crystalline PLA and PLA/Thermoplastic Starch Blends (PDF, 928 Kio)
|
---|
DOI | Trouver le DOI : https://doi.org/10.1002/mabi.200700080 |
---|
Auteur | Rechercher : Mihai, Mihaela; Rechercher : Huneault, Michel A.1; Rechercher : Favis, Basil D.; Rechercher : Li, Hongbo1 |
---|
Affiliation | - Conseil national de recherches du Canada. Institut des matériaux industriels du CNRC
|
---|
Format | Texte, Article |
---|
Résumé | Low density open-cell foams were obtained from polylactic acid (PLA) and from blends of PLA with thermoplastic starch (TPS) using CO2 as a blowing agent. Two unexpected features were found. First, a 2D cavitation process in the fractured cell walls was unveiled. Elliptical cavities with dimensions in the 100–300 nm range were aligned perpendicular to large cell cracks clearly exhibiting 2D crazing prior to macroscopic cell rupture. Secondly, a significant crystallization rate increase associated with the CO2 foaming of PLA was discovered. While the PLA used in this study crystallized very slowly in isothermal crystallization, the PLA foams exhibited up to 15% crystallinity, providing evidence that CO2 plasticization and the biaxial stretching upon foam expansion provided conditions that could increase the crystallization rate by several orders of magnitude. |
---|
Date de publication | 2007-07-09 |
---|
Dans | |
---|
Langue | anglais |
---|
Publications évaluées par des pairs | Oui |
---|
Numéro du CNRC | NRCC 53787 |
---|
Numéro NPARC | 15959409 |
---|
Exporter la notice | Exporter en format RIS |
---|
Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
---|
Identificateur de l’enregistrement | e85ef412-0117-4e65-90cd-00052529eef7 |
---|
Enregistrement créé | 2010-10-05 |
---|
Enregistrement modifié | 2020-05-10 |
---|