| DOI | Trouver le DOI : https://doi.org/10.1166/jnn.2017.14226 |
|---|
| Auteur | Rechercher : Hosseini, Arezoo1; Rechercher : Kar, Piyush1; Rechercher : Hsieh, Ling-Hsuan1; Rechercher : Wiltshire, Benjamin D.1; Rechercher : Mohammadpour, Arash1; Rechercher : Farsinezhad, Samira1; Rechercher : Benlamri, Mourad1; Rechercher : Zhang, Yun1; Rechercher : Ercelebi, C.1; Rechercher : Shankar, Karthik1 |
|---|
| Affiliation | - Conseil national de recherches du Canada. Nanotechnologie
|
|---|
| Format | Texte, Article |
|---|
| Sujet | electrodeposition; mobility; monocrystalline rutile tio2 nanowires; photovoltaic; solid-state solar cell; solvothermal growth |
|---|
| Résumé | We report a p–n heterojunction solid-state solar cell comprised of p-type CdTe that was electrochemically deposited onto hydrothermally synthesized vertically oriented arrays of n-type single crystal rutile TiO2 nanowire arrays (RNWAs). The nanowires were grown on fluorine doped tin oxide (FTO)-coated transparent conductive glass substrates by hydrothermal synthesis. Morphological studies revealed the TiO2 nanowires to be completely infiltrated by the CdTe. The solid-state solar cell exhibited an open circuit voltage of 0.6 V, a short-circuit current density of 3.57 mA cm−2, a fill factor of 44% and a power conversion efficiency of 0.96%. |
|---|
| Date de publication | 2017-07-01 |
|---|
| Maison d’édition | American Scientific Publishers |
|---|
| Dans | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Numéro NPARC | 23003285 |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | fe8966fc-3f4d-4578-8233-60383f26f423 |
|---|
| Enregistrement créé | 2018-05-10 |
|---|
| Enregistrement modifié | 2020-03-16 |
|---|