Deformation and dislocation structure in L12 titanium trialuminide alloys

Download	View accepted manuscript: Deformation and dislocation structure in L12 titanium trialuminide alloys (PDF, 1.4 MiB)
Author	Search for: Hu, Gengxiang; Search for: Chen, Shipu; Search for: Wu, Xiaohua; Search for: Rong, Yonghua; Search for: Chen, Xiaofu
Format	Text, Article
Abstract	The deformation behaviour and the nature of dislocations of the Al3Ti-base L12 alloya modified with Fe and Mn etc, were investigated. The results show that the deformation and fracture character istics are closely related to the alloy compositions. The effect of hot-working process on the room tem perature ductility is remarkable, not only resulting in an appreciable improvement of compressive properties but also showing a 0.28% plastic strain in tensile test. The SISF dissociation of a < 110>dislocations on {111} planes was found at room temperature. The determined dissociation scheme is consistent with the mechanical behaviour of these alloys in the lower temperature region.
Publication date	1994
In	Journal of Materials Science and Technology 10, no. 6 (1994): 435–440.
Language	English
NRC publication	This is a non-NRC publication "Non-NRC publications" are publications authored by NRC employees prior to their employment by NRC.
NPARC number	21276882
Export citation	Export as RIS
Report a correction	Report a correction (opens in a new tab)
Record identifier	38705f8f-bf3a-48c2-9e2a-2641c987f5a6
Record created	2015-10-30
Record modified	2020-06-04