Deformation and dislocation structure in L12 titanium trialuminide alloys

Téléchargement
  1. (PDF, 1.4 Mio)
AuteurRechercher : ; Rechercher : ; Rechercher : ; Rechercher : ; Rechercher :
FormatTexte, Article
Résumé
The deformation behaviour and the nature of dislocations of the Al3Ti-base L12 alloya modified with Fe and Mn etc, were investigated. The results show that the deformation and fracture character istics are closely related to the alloy compositions. The effect of hot-working process on the room tem perature ductility is remarkable, not only resulting in an appreciable improvement of compressive properties but also showing a 0.28% plastic strain in tensile test. The SISF dissociation of a < 110>dislocations on {111} planes was found at room temperature. The determined dissociation scheme is consistent with the mechanical behaviour of these alloys in the lower temperature region.
Date de publication
Dans
  • Journal of Materials Science and Technology 10, nº 6 (1994) : 435–440.
Langueanglais
Publication du CNRC
Cette publication n’est pas du CNRC

Ce sont des publications qui ont été rédigées par un auteur du CNRC, mais avant que celui-ci soit employé du CNRC.

Numéro NPARC21276882
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement38705f8f-bf3a-48c2-9e2a-2641c987f5a6
Enregistrement créé2015-10-30
Enregistrement modifié2020-06-04

Détails de la page

Par :

Date de modification :