| DOI | Trouver le DOI : https://doi.org/10.1016/j.matlet.2018.12.060 |
|---|
| Auteur | Rechercher : Li, Shuhan; Rechercher : Chen, Yuhua; Rechercher : Kang, Jidong; Rechercher : Amirkhiz, Babak Shalchi; Rechercher : Nadeau, Francois1 |
|---|
| Affiliation | - Conseil national de recherches du Canada. Automobile et les transports de surface
|
|---|
| Format | Texte, Article |
|---|
| Sujet | welding; advanced high strength steel; aluminum alloy; intermetallic compound; deposition; microstructure |
|---|
| Résumé | To overcome the undesirable wear of pin-tip during friction stir lap welding (FSLW) of AA6022 aluminum alloy and Usibor® 1500 advanced high strength steel, a precoated Al cold-spray deposition (200 μm in thickness) has been used as the interlayer. The optimized weld shows a simple sandwich-like structure that consists of an aluminum weld, an interface, and a heat affected steel region. No intermetallic compound was found while an Al/Fe diffusion layer with an average thickness of about 10 nm was observed at the deposition/steel interface. No distinct phase transition and mechanical properties change were found in the heat affected steel region. |
|---|
| Date de publication | 2018-12-19 |
|---|
| Maison d’édition | Elsevier |
|---|
| Dans | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | 207b945e-8a48-4ff3-ba55-8268f3289239 |
|---|
| Enregistrement créé | 2021-03-12 |
|---|
| Enregistrement modifié | 2021-03-12 |
|---|